Incazelo Yomkhiqizo
Izakhi eziyinhloko ze-alloying ye-6061 aluminium rod yi-magnesium ne-silicon, futhi zakha isigaba se-Mg2Si.Uma iqukethe inani elithile le-manganese ne-chromium, inganciphisa imiphumela emibi yensimbi;ngezinye izikhathi inani elincane lethusi noma i-zinc lengezwa ukuze kuthuthukiswe amandla e-alloy ngaphandle kokunciphisa kakhulu ukumelana nokugqwala;kusekhona inani elincane le-conductive material.I-Copper yokunciphisa imiphumela emibi ye-titanium ne-iron ku-conductivity kagesi;i-zirconium noma i-titanium ingacwenga okusanhlamvu futhi ilawule ukwakheka kabusha kwe-recrystallization;ukuze kuthuthukiswe ukusebenziseka kalula, kungangezwa umthofu kanye ne-bismuth.I-6061-T651 iyingxubevange eyinhloko ye-alloy yochungechunge oluyisi-6, futhi ingumkhiqizo wekhwalithi ephezulu we-aluminium alloy oye wenziwa ukwelashwa kokushisa kanye nokwelula kwangaphambili.Nakuba amandla ayo engenakuqhathaniswa nochungechunge lwe-2XXX kanye nochungechunge lwe-7XXX, ama-alloys ayo e-magnesium ne-silicon anezici eziningi nokusebenza okuhle kakhulu kokucubungula, izici ezinhle kakhulu zokushisela kanye ne-electroplating, ukumelana nokugqwala okuhle, ukuqina okuphezulu futhi akukho ukuguqulwa ngemva kokucubungula, izinto eziminyene ezingenasici futhi kulula ukupholisha, ifilimu elula ukufaka umbala, umphumela omuhle kakhulu we-oxidation nezinye izici ezinhle kakhulu.
I-6063 aluminium rod iwuchungechunge oluphansi lwe-Al-Mg-Si oluyingxube yepulasitiki ephezulu.Inezici eziningi ezibalulekile:
1. Kuqiniswe ukwelashwa kokushisa, ukuqina komthelela omkhulu, futhi akuzweli lapho engekho.
2. Nge-thermoplasticity enhle kakhulu, ingakhishwa ngesivinini esikhulu ibe amaphrofayili ayinkimbinkimbi, anezindonga ezincane futhi angenalutho noma ihlanganiswe ibe yi-forging enesakhiwo esiyinkimbinkimbi, ububanzi obubanzi bokushisa okucishayo, ukuzwela okuphansi kokucisha, ngemva kokukhipha kanye nokukhwabanisa, inqobo nje izinga lokushisa. iphakeme kunezinga lokushisa lokucisha.Ingacinywa ngesifutho samanzi noma ukungena kwamanzi.Izingxenye ezinezindonga ezincane (6<3mm) nazo zingacishwa umoya.
3. Ukusebenza okuhle kakhulu kwe-welding kanye nokumelana nokugqwala, akukho ukuthambekela kokuqhekeka kokugqwala kokucindezeleka.Phakathi kwama-alloys e-aluminium anamandla okuphulukiswa ngokushisa, ama-alloys e-Al-Mg-Si yiwona kuphela ama-alloys angatholanga ukuqhekeka kokugqwala kwengcindezi.
4. Ubuso ngemva kokucubungula bushelelezi kakhulu futhi kulula uku-anodize nombala.
Ukwakheka kwamakhemikhali kanye nezakhiwo zemishini ye-6061 aluminium rod
Al | Si | Cu | Mg | Zn | Mn | Cr | Fe | Ti |
Isibonelelo | 0.4-0.8 | 0.15-0.4 | 0.8-1.2 | 0.25 | 0.15 | 0.04-0.35 | 0.7 | 0.15 |
Amandla aqinile σb | ≥180MPa |
Amandla esivuno σ0.2 | ≥110MPa |
Ubude δ5 (%) | ≥14 |
I-Elasticity coefficient | 68.9 GPA |
Amandla okugoba okugcina | 228 MPa |
Ukuzala Amandla Okukhiqiza | 103 MPa |
Amandla okukhathala | 62.1 MPa |
Usayizi wesampula | ububanzi: ≤150 |
Ukwakheka kwamakhemikhali kanye nezakhiwo zemishini ye-6063 aluminium rod
Al | Si | Cu | Mg | Zn | Mn | Cr | Fe | Ti |
Isibonelelo | 0.2-0.6 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.35 | 0.1 |
Amandla e-Tensile σb (MPa) | 130-230 |
Inani eliphakeme kakhulu lama-6063 | 124 MPa |
Amandla esivuno esiqinile | 55.2 MPa |
Ukwelula | 25.0 % |
I-Elasticity coefficient | 68.9 GPA |
Ukuzala Amandla Okukhiqiza | 103 MPa |
Isilinganiso sikaPoisson | 0.330 |
Amandla okukhathala | 62.1 MPa |