I-5052 aluminium rod iwuchungechunge lwe-AL-Mg, okuyi-aluminium elwa nokugqwala esetshenziswa kakhulu.Le alloy inamandla amakhulu, ikakhulukazi ukumelana nokukhathala: ipulasitiki ephezulu kanye nokumelana nokugqwala, futhi ayikwazi ukuqiniswa ukwelashwa kokushisa.Ipulasitiki enhle, ipulasitiki ephansi ngesikhathi sokuqina komsebenzi obandayo, ukumelana nokugqwala okuhle, ukushisela okuhle, ukusebenza kabi, nokupholisha.Izinduku ze-aluminium ezingu-5052 zisetshenziselwa ikakhulukazi izingxenye ezinomthwalo ophansi ezidinga ipulasitiki ephezulu kanye nokushiselwa okuhle, futhi zisebenza emithonjeni ewuketshezi noma yegesi, njengamabhokisi eposi, uphethiloli noma amapayipi kawoyela okugcoba, iziqukathi ezihlukahlukene zoketshezi nezinye izingxenye ezincane ezenziwe ngomdwebo ojulile.Izingxenye ezilayishiwe: Ucingo lusetshenziselwa ukwenza ama-rivets.Iphinde isetshenziswe ezingxenyeni zeshidi lensimbi yezimoto zokuhamba nemikhumbi, amathuluzi, abakaki belambu lomgwaqo kanye nama-rivets, imikhiqizo ye-hardware, izivalo zikagesi, njll.
I-5083 aluminium induku ingeye-Al-Mg-Si ingxubevange, esetshenziswa kabanzi, ikakhulukazi imboni yezokwakha ayikwazi ukwenza ngaphandle kwale alloy, futhi iyingxubevange ethembisa kakhulu.Ukumelana nokugqwala okuhle, ukushisela okuhle kakhulu, ukusebenza kahle okubandayo, namandla amaphakathi.Ingxenye eyinhloko ye-alloying ye-5083 yi-magnesium, enokwakheka okuhle, ukumelana nokugqwala, ukushisela, namandla aphakathi.Imikhiqizo yezingxenyekazi zekhompuyutha, izivalo zikagesi, njll.
Ukwakheka kwamakhemikhali kanye nezakhiwo zemishini ye-5052 aluminium rod
Al | Si | Cu | Mg | Zn | Mn | Cr | Fe |
Isibonelelo | ≤0.25 | ≤0.10 | 2.2~2.8 | ≤0.10 | ≤0.10 | 0.15-0.35 | ≤0.40 |
Amandla e-tensile (σb) | 170-305MPa |
Amandla esivuno anemibandela | σ0.2(MPa)≥65 |
Imoduli ye-elastic (E) | 69.3-70.7Gpa |
Izinga lokushisa le-anealing | 345°C. |
Ukwakheka kwamakhemikhali kanye nezakhiwo zemishini ye-5083 aluminium rod
Al | Si | Cu | Mg | Zn | Mn | Cr | Fe | Ti |
Isibonelelo | 0.4 | 0.1 | 4.0--4.9 | 0.25 | 0.40--0.10 | 0.05--0.25 | 0.4 | 0.15 |
Amandla e-Tensile σb (MPa) | 110-136 |
Ubude δ10 (%) | ≥20 |
Izinga lokushisa le-anealing | 415°C. |
Amandla esivuno σs (MPa) | ≥110 |
Isifanekiso Esingenalutho Ubukhulu Bonke Ubukhulu Bodonga | |
Ubude δ5 (%) | ≥12 |