Incazelo Yomkhiqizo
Uchungechunge lwe-1000 lungolochungechunge olunokuqukethwe kwe-aluminium kakhulu.Ukuhlanzeka kungafinyelela ngaphezu kwama-99.00%.Njengoba ingenazo ezinye izakhi zobuchwepheshe, inqubo yokukhiqiza ilula futhi intengo ishibhile.Iwuchungechunge olusetshenziswa kakhulu ezimbonini ezijwayelekile.Iningi elijikelezayo emakethe liwuchungechunge lwe-1050 no-1060.Izinti ze-aluminium ezingu-1000 zochungechunge zinquma ubuncane bokuqukethwe kwe-aluminium kulolu chungechunge ngokwezinombolo zokugcina ezimbili zesi-Arabhu.Isibonelo, izinombolo zokugcina ezimbili zesi-Arabhu zochungechunge lwe-1050 zingu-50. Ngokomgomo wamazwe ngamazwe wokuqamba igama lomkhiqizo, okuqukethwe kwe-aluminium kufanele kufinyelele ngaphezu kuka-99.5% ukuze kube imikhiqizo efanelekayo.izinga lobuchwepheshe bezwe lami le-aluminium alloy (gB/T3880-2006) nalo libeka ngokucacile ukuthi okuqukethwe kwe-aluminium engu-1050 kufanele kufinyelele ku-99.5%.
Ngesizathu esifanayo, okuqukethwe kwe-aluminium kwezinduku ze-aluminium ezingu-1060 kufanele kufinyelele ngaphezu kwama-99.6%.Izici ze-1050 Industrial aluminium ehlanzekile inezici ezijwayelekile ze-aluminium, njengokuminyana okuphansi, ukuhanjiswa okuhle kukagesi nokushisayo, ukumelana nokugqwala okuhle, nokusebenza kahle kwepulasitiki.Ingacutshungulwa ibe amapuleti, amapheshana, ama-foil kanye nemikhiqizo ekhishwe, futhi ingasetshenziselwa ukushisela igesi, i-argon arc welding kanye nokushisela indawo.
Ukusetshenziswa kwe-aluminium engu-1050 1050 kuvame ukusetshenziswa ezidingweni zansuku zonke, izinto ezikhanyayo, izibonisi, imihlobiso, iziqukathi zamakhemikhali, amasinki okushisa, izimpawu, izinto zikagesi, izibani, ama-nameplates, izinto zikagesi, izingxenye zokugxiviza neminye imikhiqizo.Kwezinye izikhathi lapho ukumelana nokugqwala kuyadingeka ngesikhathi esifanayo, kodwa izidingo zamandla zingekho phezulu, okokusebenza kwamakhemikhali kuwukusetshenziswa kwayo okuvamile.
I-aluminium ehlanzekile engu-1060: i-aluminium ehlanzekile yezimboni inezici ze-plasticity ephezulu, ukumelana nokugqwala, ukuguquguquka okuhle kukagesi nokushisayo, kodwa amandla aphansi, akukho ukuqinisa ukwelashwa kokushisa, ukungahambi kahle komshini, kanye ne-welding yokuxhumana eyamukelekayo kanye nokushisela igesi.Ukusetshenziswa okwengeziwe kwezinzuzo zayo ukwenza ezinye izingxenye zesakhiwo ezinezakhiwo ezithile, njengama-gaskets nama-capacitor enziwe nge-aluminium foil, amanetha ahlukanisa ama-valve, izintambo, amajakhethi okuvikela amakhebula, amanethi, ama-wire cores kanye nezingxenye zesistimu yokukhipha umoya wendiza kanye nezinsimbi.
Ukusebenza okubandayo kuyindlela ejwayelekile kakhulu yokwenza i-Aluminium 1100. Inqubo yokusebenza kwensimbi ebandayo yinoma iyiphi inqubo yokwakha insimbi eyenziwa ekamelweni lokushisa noma eliseduze.I-Aluminium 1100 ingakhiwa ibe yimikhiqizo eminingi ehlukene, okuhlanganisa okokusebenza kwamakhemikhali, izimoto zamathangi kaloliwe, izindiza ezingemuva, amadayili, ama-nameplates, ama-cookware, ama-rivets, izibonisi neshidi lensimbi.I-Aluminium 1100 isetshenziswa nasezimbonini zamapayipi kanye nezibani, njengoba kunjalo nakwezinye izimboni ezahlukahlukene.
I-Aluminium 1100 ingenye yezinto ezithambile ze-aluminium ngakho-ke ayisetshenziselwa amandla aphezulu noma izinhlelo zokusebenza zokucindezela okuphezulu.Nakuba ngokuvamile kubanda, i-aluminium ehlanzekile ingabuye ishise, kodwa ngokuvamile, i-aluminium yenziwa ngokuphotha, ukugxiviza nokudweba izinqubo, okungekho okudinga ukusetshenziswa kwamazinga okushisa aphezulu.Lezi zinqubo zikhiqiza i-aluminium ngesimo se-foil, ishidi, nxazonke noma ibha, ishidi, i-strip nocingo.I-Aluminium 1100 nayo ingashiselwa;ukumelana nokushisela kungenzeka, kodwa kungase kube nzima futhi ngokuvamile kudinga ukunakwa komshiseli onekhono.I-Aluminium 1100 ingenye nje yama-alloys ambalwa avamile athambile, anamandla aphansi futhi, ku-99% i-aluminium, ahlanzekile kwezohwebo.Izakhi ezisele zihlanganisa ithusi, insimbi, i-magnesium, i-manganese, i-silicon, i-titanium, i-vanadium ne-zinc.
Ukubunjwa Kwekhemikhali kanye Nempahla Yemishini 1060
Al | Si | Cu | Mg | Zn | Mn | Ti | V | Fe |
99.50 | ≤0.25 | ≤0.05 | ≤0.05 | ≤0.05 | ≤0.05 | ≤0.03 | ≤0.05 | 0.00-0.40 |
I-TensileStrength(Mpa) | 60-100 |
EL(%) | ≥23 |
Ukuminyana(g/cm³) | 2.68 |
Ipharamitha yomkhiqizo1050
Ukwakheka Kwamakhemikhali | |||||
Ingxubevange | Si | Fe | Cu | Mn | Mg |
1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 |
Zn | -- | Ti | Ngamunye | Ingqikithi | Al. |
0.05 | 0.05V | 0.03 | 0.03 | - | 99.5 |
Izakhiwo zemishini
Amandla e-Tensile σb (MPa): 110~145.Ubude δ10 (%): 3~15.
Imininingwane yokwelashwa kokushisa:
1. Qedela i-anealing: ukushisa okungu-390 ~ 430℃;kuye ngokuqina okusebenzayo kwezinto, isikhathi sokubamba singama-30 ~ 120min;ukupholisa ngesithando somlilo kuye ku-300℃ ngesilinganiso esingu-30~50℃/h, bese kuba ukupholisa umoya.
2. Ukufakwa kwe-anneal ngokushesha: ukushisa okungu-350~370℃;kuye ngokuqina okusebenzayo kwezinto, isikhathi sokubamba singama-30 ~ 120min;ukupholisa umoya noma amanzi.
3. Ukucisha nokuguga: ukucisha i-500 ~ 510 ℃, ukupholisa umoya;ukuguga okwenziwe 95 ~ 105 ℃, 3h, ukupholisa umoya;izinga lokushisa lemvelo lokuguga 120h